xPEEK147 SLA Resin for XiP – 1Kg

349.34

xPEEK147 SLA Resin is a cutting-edge 3D printing material designed for high-temperature applications and demanding industrial environments. With a Heat Deflection Temperature (HDT) of 230ºC, it boasts exceptional thermal stability, making it suitable for a wide range of applications where traditional plastics would deform or fail under heat stress.

This resin is a game-changer for industries that require parts and prototypes that can withstand extreme temperatures. It has an impressive tensile modulus of 3190 MPa, providing high stiffness, and an ultimate tensile strength of 75 MPa, ensuring durability and reliability. Its flexural properties, with a flex modulus of 2170 MPa and flexural strength of 130 MPa, make it ideal for applications like fast tooling for plastic moulding, where precision and heat resistance are paramount.

One of the key advantages of xPEEK147 is its long-term stability at temperatures exceeding 100ºC. This characteristic is invaluable for industries like aerospace, automotive, and manufacturing, where parts must perform reliably under extreme conditions. Whether you need functional prototypes, end-use parts, or fast tooling for injection moulding, xPEEK147 delivers exceptional results.

Please note that xPEEK147 requires post-print baking to ensure complete polymerization. This thermal post-processing step is crucial to achieving the material’s full performance potential. If you have any questions or need recommendations regarding the baking process, don’t hesitate to reach out to our support team.

In summary, xPEEK147-Black Resin is a versatile and high-performance material that opens up new possibilities for 3D printing in industries where extreme heat resistance and mechanical properties are essential. Its exceptional HDT, tensile strength and thermal stability make it a game-changing solution for applications that demand the utmost in performance and reliability.

Property Value Test Method
Tensile Modulus 3190 MPa ASTM D638
Ultimate Tensile Strength 75 MPa ASTM D638
Tensile Elongation at Break 3% ASTM D638
Flex Modulus 2170 MPa ASTM D790
Flex Strength 130 MPa ASTM D790
Hardness (Shore D) 94 ASTM D2240
Notched Izod 15 J/m ASTM D256
HDT @0.45 MPa 238ºC ASTM D648
Water Absorption 0.25% ASTM D570